Art Paper for Large Wood Relief Block Printing – A Paper Development Study
Klaus Dölle *
Department of Chemical Engineering (CHE), College of Environmental Science and Forestry (ESF), State University of New York (SUNY), One Forestry Drive, Syracuse, NY 13210, USA.
Hélène Rainville
Department of Chemical Engineering (CHE), College of Environmental Science and Forestry (ESF), State University of New York (SUNY), One Forestry Drive, Syracuse, NY 13210, USA.
*Author to whom correspondence should be addressed.
Abstract
Wood relief block printing was developed in China in the seventh century and is used today for many art printing applications. The presented research project describes the development of an art paper product applicable for large wood relief block printing from laboratory scale to large semi commercial production of art paper for printing image sizes of up to 44-inch (1118 mm) by 96-inch (2400 mm) at outdoor steam roller printing events or smaller indoor printing press applications.
The improvement of the paper properties from laboratory development, small laboratory paper machine and semi commercial paper machine run for the production of the final art paper showed an improvement throughout the process development for the optical and mechanical paper properties and exceeded the set values set by the artist using the art paper.
The produced art paper with a basis weight of 260 g/m² and a thickness of 171 µm is produced from a mixture of 70% northern bleached hardwood Kraft pulp and 30% northern bleached softwood Kraft pulp.
The ISO brightness of the art paper off-white (egg-shell) colour was at 63.2% and the ISO color value for L, a, b. at 90.8, 1.1, and 12.6 respectively.
The art papers surface roughness and porosity as a parameter for ink attachment and penetration is for the top side 2179 ml/min and for the bottom side (wire side) 2326 ml/min, whereas porosity was measured at 1668 ml/min.
Bending stiffness in machine direction and cross machine direction was measured at 157mN and 70 mN respectively. Burst strength was measured at 2.24 kPA·m²/g.
Keywords: Art paper, papermaking, paper machine, printing, wood relief block printing.